POLYLINK
POLYMERS (INDIA) LTD. Products
Polypropylene
Filled Compounds
Mineral Filled
Polypropylene Compounds
Glass Filled
Polypropylene Compounds
40%
Talc Filled Polypropylene Homopolymer
Grade - P - 11040CT
DESCRIPTION
:
P-11040CT is manufactured by compounding polypropylene homopolymer with fine grade of 10 micron talc. Additives like antioxidant,
lubricant, processing aid and desiccant are added to improve long term thermal and process ability. The compound when diluted with desired grades of polypropylene shows good dispersibility and excellent balance of properties in the ultimate product.
SPECIAL CHARACTERISTICS :
The filler in the compound incorporates certain important properties those are essential for ultimate product. The modifications are as below:
| Improves
|
Reduces
|
| Mechanical properties
|
Cost
|
| Dimensional stability
|
Cycle time
|
TECHNICAL DATASHEET :
Property |
Test
Method |
Unit |
Typical
value |
Special
Gravity |
ASTM-D-792 |
gm / cm3 |
1.12 |
|
MFI at 190°
C / 2.16 Kg. |
ASTM-D-1238 |
G / 10 min |
8 - 10 |
|
Moisture
Content |
PPIL |
ppm |
<600 |
|
Filter
Content |
TGA |
% |
40.5 |
|
Colour |
Visual |
|
white |
|
Flex. Mod. |
ASTM-D-790 |
Kg/ cm2 |
34,000 |
|
Flex.
Strength |
ASTM-D-790 |
Kg/
cm2 |
400 |
|
Izod Impact
Strength Notched |
ASTM-D-256 |
Kg/ cm2 |
3.00 |
|
Tensile Strength |
ASTM-D-638 |
Kg/ cm2 |
190 |
|
Elongation
at break |
ASTM-D-638 |
% |
5 |
Drying :
The compound should be dried 70 deg C for 30 min in hopper prior to its use.
Storage :
The material shall be dried in a dry cool place.
FORM AND PACKING :
Delivery form :
The material is supplied in the form of pellets
Packing :
In 25 Kg HDPE/PP woven sacks
This information is to the best of our knowledge. The values of different parameters and operating conditions listed above are guidance only and should not be used for drawing specifications. The results & operating conditions may vary depending on methods of test and manufacturing / testing equipments.
Mineral
Filled Polypropylene Compounds
Glass
Filled Polypropylene Compounds
|